High Temperature Resistance Alumina Fire Brick
China supplied high temperature resistance alumina fire brick for boiler with competitive price Introduction to alumina fire brick Alumina fire brick is a kind of refractory material. It is an aluminum silicate refractory product with aluminum oxide (Al2O3) content higher than 48%. The main...
China supplied high temperature resistance alumina fire brick for boiler with competitive price
High Temperature Resistance Alumina Fire Brick
Introduction to alumina fire brick
Alumina fire brick is a kind of refractory material. It is an aluminum silicate refractory product with aluminum oxide (Al2O3) content higher than 48%. The main component of this refractory brick is AL2O3.. It is formed and calcined from alumina or other raw materials with high alumina content. High thermal stability, refractoriness above 1770℃. It has good slag resistance and is used for lining steel-making electric furnaces, glass melting furnaces, cement rotary furnaces, etc.
Product performance of alumina fire brick
1. Refractoriness of alumina fire brick
The refractoriness of alumina fire brick is higher than that of clay bricks and semi-silica bricks, at 1750~1790℃, which belong to advanced refractory materials.
2. Load softening temperature of alumina fire brick
Because high-alumina products have high Al2O3, less impurities, and less fusible glass bodies, the load softening temperature is higher than that of clay bricks. alumina fire brick, but because mullite crystals do not form a network structure, there is still no silicon at the load softening temperature. Brick high.
3. Slag resistance of alumina fire brick
alumina fire brick contain more Al2O3, which is close to neutral refractory materials, and can resist the erosion of acidic slag and alkaline slag. Because of the inclusion of SiO2, the ability to resist alkaline slag is weaker than that of acidic slag.
Classification of alumina fire brick
1. Classified by Al2O3 content in alumina fire brick
ClassⅠ: Al2O3 content>75%
ClassⅡ: Al2O3 content is 60~75%
ClassⅢ: Al2O3 content is 48-60%.
If Al2O3 content is higher than 80%, it is called super alumina fire brick
If Al2O3 content is higher than 90%, it is called corundum brick.
2. Classification of alumina fire brick by firing process
It can be divided into fired alumina fire brick and unfired alumina fire brick. The firing temperature of the first and second grade alumina fire brick is 1500℃-1600℃ and 1450℃-1500℃ respectively, while the third grade is lower. High-alumina non-sintered bricks mainly refer to phosphate high-alumina.
3. Classification of alumina fire brick by mineral composition
It can be divided into five types: low mullite, mullite, mullite, corundum, corundum and corundum;
4. Classification of alumina fire brick according to different shapes
It can be divided into standard alumina fire brick, special-shaped alumina fire brick and special alumina fire brick;
5. Classification of alumina fire brick according to their properties
It can be divided into ordinary alumina fire brick and special alumina fire brick (thermal shock resistance, low creep, anti-stripping alumina fire brick;
6. Classification of alumina fire brick by use
It can be divided into high-aluminum and high-alumina bricks, hot-blast stove high-alumina bricks, steel-making electric furnace top high-alumina bricks, Shenggang barrel high-alumina bricks, and inner cast high-alumina bricks.
Technical Data Sheet
Technical Data Sheet of alumina fire brick
Grade | SK-32 | SK-34 | SK-36 | SK-38 | SK-40 |
Al2O3 % ≥ | 48 | 55 | 65 | 75 | 80 |
Fe2O3 % ≤ | 2.5 | 2.0 | 1.8 | 1.6 | 1.5 |
Refractoriness (℃) ≥ | 1770 | 1770 | 1770 | 1790 | 1790 |
Apparent Porosity % ≤ | 24 | 23 | 23 | 22 | 21 |
Bulk Density (g/cm3) ≥ | 2.15-2.25 | 2.25-2.35 | 2.35-2.45 | 2.45-2.65 | 2.65-2.75 |
Cold Crushing Strength (Mpa) ≥ | 35 | 40 | 45 | 55 | 60 |
Refractoriness Under Load 0.2Mpa (℃) ≥ | 1300 | 1350 | 1400 | 1490 | 1530 |
Permanent Linear Change % | 1300℃×2h | 1350℃×2h | 1400℃×2h | 1500℃×2h | 1550℃×2h |
+0.1~-0.4 | +0.1~-0.4 | +0.1~-0.4 | +0.1~-0.4 | +0.1~-0.4 |
Application of alumina fire brick
alumina fire brick are mainly used to build blast furnaces, hot blast stoves, electric furnace tops, blast furnaces, reverberatory furnaces, rotary kiln linings, cement rotary kiln transition zones, preheaters and other thermal equipment requiring heat shock resistance; in addition, alumina fire brick are also widely used as open hearth regenerative checker bricks, plugs for pouring systems, nozzle bricks, etc.
Delivery
Package Informations:
1. Packed in a 100cm*100cm fumigated wooden pallet with a waterproof plastic film cover, and tightened with plastic bandages.
2. We can also pack the goods according to your requirements.
Shipping
1. FEDEX/DHL/UPS/TNT for samples.
2. By Sea for batch goods.
3. Customers specifying freight forwarders or negotiable shipping methods!
4. Delivery Time:3 days for common shape samples;15 days for special shape samples.Within 30 days for batch goods.
FAQ:
Q: What's the MOQ?
A: No limitation.
Q: What's your payment terms?
A:Negotiation
A: For every production processing,we have complete QC system for the chemical composition and Physical properties.After production,all the goods will be tested ,and the quality certificate will be shipped along with goods.
Q: Does your FOSHAN HUANYA Refractory Material Co., Ltd. supply samples?
A: Yes, we can supply samples for free, and the freight will be undertaken by clients.
Contact us:
Martin
Tel:8613923217470
Email: Martin@huanya-refractory.com
Adderss:4A02, 4A Floor, Ruiying Commercial Building, Dali Town, Nanhai District, Foshan City, Guangdong, China
Hot Tags: high temperature resistance alumina fire brick, China, manufacturers, factory, customized, wholesale, low price, in stock, free sample, Alumina Burner Blocks Brick, Fire Pure Anchor Brick For Kiln Furnace, 80 High Aluminum Brick, High Temperature Resistant Glass Kiln AZS Brick, White Refractory Brick Alumina Bubble Brick, Density High Alumina Bauxite Bricks